alkaline bath

Copper Electroplating in Alkaline Bath Containing Novel Brightening Agent

采用新型组合光亮剂的碱性镀铜研究

A Study on Dyeing Property of Superfine Fiber with Disperse Dye in Alkaline Bath

超细纤维织物国产分散染料碱性浴染色性能研究

Transparent and thin copper layer in various colours can be electroplated onto stainless steel surfaces from an alkaline bath with low current density.

在碱性铜盐溶液中以低电流密度对不锈铜进行电镀可获得多种彩色鲜艳的透明薄铜层。

Studies on white chromating of zinc-nickel alloy electrodeposited from alkaline bath

碱性锌镍合金电镀白钝化工艺的研究

The changes of surface potential and topography of Fe-Mo amorphous alloy coatings deposited In original alkaline bath at room temperature were investigated.

研究了非晶态Fe-Mo合金镀层在室温下的原碱性镀液中或其他溶液介质中的表面电位、表面形貌的变化。

The Technology and Properties of Superfine Polyester Fabric Dyed in Alkaline Bath

超细涤纶织物碱性浴染色工艺研究

The zinc nickel alloy depositions with grain size of 14-33 nm were electroplated by using adequate additives in an alkaline bath.

采用适当的添加剂在碱性体系中获得了晶粒度为14&33nm的纳米锌镍合金电镀层。

Further more, the ratio of the main compositions of the alkaline bath is very important for its tempering effect. The results strongly indicate that the contents of alkali and the anti-oxidation reagent can significantly affect the hardness.

碱浴的配比很重要，其中碱和脱氧剂的用量对回火硬度影响显著。

New Application Technology of Chemical Nickel phosphorus Plating from alkaline bath at Middle Temperature

中温碱性化学镀镍磷实用新工艺研究

Electrodeposition of Zn-Ni Alloy in alkaline bath

碱性锌镍合金电镀

And the coating obtained in alkaline bath is of crystal structure, belonging to low phosphorous coating.

在碱性镀液中获得的镀层是晶态的，属于低磷镀层。

Selection of Formulation of Combined Additives for Electroplating of Zinc-Nickel Alloy Coating from an Alkaline Bath

碱性体系中锌镍合金电镀添加剂复合配方优选